| 李宪,高磊,刘迎云,周凌峰,易磊,解金柯,李彩亭.秸秆生物质炭室温吸附气态甲醛的研究[J].南华大学学报(自然科学版),2021,(2):16~24.[LI Xian,GAO Lei,LIU Yingyun,ZHOU Lingfeng,YI Lei,XIE Jinke,LI Caiting.A Comparative Study on Adsorbing Formaldehyde with Novel Agriculture Wastes Derived Biomass Activated Carbons at Indoor Temperature[J].Journal of University of South China(Science and Technology),2021,(2):16~24.] |
| 秸秆生物质炭室温吸附气态甲醛的研究 |
| A Comparative Study on Adsorbing Formaldehyde with Novel Agriculture Wastes Derived Biomass Activated Carbons at Indoor Temperature |
| 投稿时间：2020-12-23 |
| DOI：10. 19431/ j. cnki. 1673-0062. 2021. 02. 003 |
| 中文关键词: 化学活化 生物质活性炭 甲醛 〖PS李宪二维码.tif Y4*4,Y#〗 |
| 英文关键词:chemical activation biomass activated carbon formaldehyde |
| 基金项目:国家重点研发计划(2016YFC0204104)；湖南省自然科学基金(2020JJ5487)；湖南省教育厅科研项目(19C1611)；湖南省教育厅科研重点项目(17A180) |
| 作者 | 单位 | E-mail | | 李宪 | 南华大学 资源环境与安全工程学院,湖南 衡阳 421001
污染控制与修复衡阳重点实验室,湖南 衡阳 421001 | | | 高磊 | 南华大学 资源环境与安全工程学院,湖南 衡阳 421001
污染控制与修复衡阳重点实验室,湖南 衡阳 421001 | | | 刘迎云 | 南华大学 资源环境与安全工程学院,湖南 衡阳 421001
污染控制与修复衡阳重点实验室,湖南 衡阳 421001 | gxylyy0924@126.com | | 周凌峰 | 南华大学 资源环境与安全工程学院,湖南 衡阳 421001
污染控制与修复衡阳重点实验室,湖南 衡阳 421001 | | | 易磊 | 南华大学 资源环境与安全工程学院,湖南 衡阳 421001
污染控制与修复衡阳重点实验室,湖南 衡阳 421001 | | | 解金柯 | 南华大学 资源环境与安全工程学院,湖南 衡阳 421001 | | | 李彩亭 | 湖南大学 环境科学与工程学院,湖南 长沙 410082 | |
|
| 摘要点击次数: 818 |
| 全文下载次数: 330 |
| 中文摘要: |
| 研究采用ZnCl2活化农业秸秆废弃物的方法制备高比表面积的生物质炭(BACs),以实现室温下高效吸附气态甲醛。工业分析和元素分析表明所用农业秸秆是适宜的BACs前体物,且比表面积、扫描电镜、傅里叶红外光谱和热重分析结果表明BACs能够实现理想吸附效果。系统性实验探究了活化条件、O2和气态甲醛浓度对BACs吸附性能的影响,结果表明,ZnCl2/RPm质量比、活化温度和时间对吸附性能有显著的正向影响,而O2对吸附性能有抑制作用;随着HCHO浓度的增加,BACs的吸附性能单位时间内损失率增大。对饱和BACM(玉米秸秆提取的BAC)进行脱附和再生试验,结果得出,解吸温度均在50 ℃以上,能够保证室内使用安全;饱和BACM经再生后,仍表现出较好的吸附性能,表明该吸附剂可重复利用。 |
| 英文摘要: |
| To effectively remove indoor formaldehyde (HCHO) at ambient temperature and reasonably use agriculture wastes, a series of high specific surface area biochars (BACs) are prepared with agriculture straws as raw materials and ZnCl2 as activator. These agricultural straws was presumed to be appropriate BACs precursors by proximate analysis and ultimate analysis. Physicochemical properties were characterized by BET, SEM, FTIR and TGA, which demonstrated BACs had the potential as brilliant adsorbents. Systemic tests investigated the effects of activator and the concentrations of O2 and HCHO on adsorption performances of BACs. Results showed ZnCl2 brought considerably positive effects but O2 had a depressant effect on the adsorption behavior. With the increase of HCHO concentration, the loss rate of adsorption property in BACs increased per unit time. Desorption and regeneration tests indicated that the desorption temperature all above 50 ℃, ensureing security indoors. Saturated BACM still exhibited remarkable adsorption performance after regeneration, indicating that the adsorbent can be reused. |