| 吴红枚,陈解放,陈少云,刘芝芳,王孟,李飞,吴斌.HMDI-IPDI型阳离子水性聚氨酯的合成及性能[J].南华大学学报(自然科学版),2014,28(4):74~80.[WU Hong-mei,CHEN Jie-fang,CHEN Shao-yun,LIU Zhi-fang,WANG Meng,LI Fei,WU Bin.Synthesis and Properties of Cationic WaterbornePolyurethane Based on HMDI-IPDI[J].Journal of University of South China(Science and Technology),2014,28(4):74~80.] |
| HMDI-IPDI型阳离子水性聚氨酯的合成及性能 |
| Synthesis and Properties of Cationic WaterbornePolyurethane Based on HMDI-IPDI |
| 投稿时间：2014-02-28 |
| DOI： |
| 中文关键词: 阳离子水性聚氨酯 固含量 断裂伸长率 吸水率 |
| 英文关键词:cationic waterborne polyurethane solid content breaking elongation water absorption |
| 基金项目:国家自然科学基金资助项目(21104031);湖南省自然科学基金资助项目(08JJ4024) |
|
| 摘要点击次数: 976 |
| 全文下载次数: 1211 |
| 中文摘要: |
| 以异佛尔酮二异氰酸酯(IPDI)、4,4-二环己基甲烷二异氰酸酯(HMDI)、聚醚二元醇(PTMEG-2000)为单体,用N-甲基二乙醇胺作亲水扩链剂,制备阳离子型水性聚氨酯(WPU),并对其进行了红外光谱和粒径分析,主要探讨了影响阳离子水性聚氨酯固含量、断裂伸长率、吸水率的因素如混合二异氰酸酯摩尔比n(IPDI/HMDI)、预聚时二异氰酸酯与二元醇摩尔比n(二异氰酸酯/二元醇)、N-甲基二乙醇胺用量、三羟甲基丙烷用量和中和度.结果表明:当n(IPDI/HMDI)在0.47∶1与0.23∶1之间时,所制得的阳离子型水性聚氨酯的固含量、断裂伸长率和吸水率均呈较稳定的状态；预聚阶段n(二异氰酸酯/二元醇)对WPU固含量影响不大,对断裂伸长率、吸水率影响明显；MDEA的用量对固含量、断裂伸长率和吸水率都有较深的影响；TMP的用量对WPU膜的固含量、吸水率及断裂伸长率影响一般；中和度对WPU固含量以及断裂伸长率的影响不大,但对吸水率影响较大. |
| 英文摘要: |
| Cationic waterborne polyurethanes have been synthesized by the step-growth polyaddition process of isophorone diisocyanate and dicyclohexylmethylmethane-4,4′-diisocyanate and polyether dibasic alcohol with N- methyl diethanolamine as hydrophilic chain extender.Infrared spectrum and particle size of WPU were analyzed.The influence of different factors affecting the solid content,breaking elongation,water absorption of the synthesized cationic waterborne polyurethane are discussed,including the mole ratios of isophorone diisocyanate and dicyclohexylmethylmethane-4,4′-diisocyanate,the mole ratios of diisocyanates and diols during prepolymerization,the dosage of N - methyl diethanolamine,the dosage of trimethylolpropane and the neutralization degree.The results show that when n(IPDI/HMDI) lies between 0.47∶1 and 0.23∶1,the solid content,the breaking elongation and water absorption are quite stable.The mole ratios of diisocyanates and diols during prepolymerization have little effect on the solid content while have an obvious effect on the breaking elongation and water absorption.The amount of MDEA has a deep influence on the solid content,the breaking elongation and water absorption.The amount of TMP has a small influence on the solid content,the breaking elongation and water absorption.The neutralization degree affects the solid content and breaking elongation slightly,but it has a greater impact on the water absorption rate. |